Use Halocell Energy’s Transparent Titania Paste is formulated to yield sintered film thicknesses of 6-7μm when screen printed with a 43T mesh. Halocell Energy’s Transparent Titania Paste has highly dispersed and stable anatase nanoparticles. It is optimised for screen printing using a synthetic 43T mesh screen (or similar). After drying, this paste must be fired at or above 500°C. This results in a transparent sintered layer, with a film thickness of approximately 6-7μm for one printed layer and ~12μm for two printed layers, when using a 43T mesh screen. The paste exhibits optimal rheological properties that provide good surface uniformity and contains organic binders specially formulated to provide versatile porosity suitable for a range of dye/electrolyte systems.